Cold Rolling Electric Silicone Steel Coil
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Jiangsu
-
Validity to:
Long-term effective
-
Last update:
2017-10-27 09:57
-
Browse the number:
244
+
Zhangjiagang Shilong Machinery Co., Ltd.
- Contactaixin:
Mrs. Smile(Mr.)
- Email: telephone: phone:
-
Arrea:
Jiangsu
Address:3#, Jinxiu Road, Jiangsu Yangtze International Metallurgical Industrial Park, Suzhou, Jiangsu, China 215600
- Website:
+
Breif Introduction
Silicon Steel Coil is steel with silicon added to it. The addition of silicon to steel increases its electrical resistance, improves the magnetic flux strength, and reduces the steel's hysteresis loss. Hysteresis is the lag between the times when a magnetic field is first generated or applied to the steel and when the field fully develops. Through control of the grain size, the hysteresis loss of the steel can be accurately controlled. The direction of the grain in Silicon Steel can also affect its efficiency. The grain can be oriented in one or double direction (CRGO) through rolling to improve its density or the grain can be non-oriented and run in all directions (CRNGO), making the Silicon Steel less expensive.
Specifications
1. Grades: 50W800
2. Thickness: 0.5mm&0.65mm
3. Width: 1000mm&1200mm
4. Inner Diameter: 508mm
5. Weight of Steel Coil: 3-8MT
Parameters
1. Density: 7.8kg/dm3
2. Iron Loss: 4.507W/Kg (f=50Hz B=1.5T)
3. Magnetic Flux Strength: 1.703T (f=50Hz H=5000A/M)
4. Interlayer Resistance: >10Ω . Cm2/piece
5. Yield Strength: 250MPa
6. Tensile Strength: 360MPa
7. Extended Length 39% (380MPa)
8. HV1 Hardness: 122
8. Lamination Factor: 97%
9. Minimum number of Bends: 10Times
Silicon Steel Coil is steel with silicon added to it. The addition of silicon to steel increases its electrical resistance, improves the magnetic flux strength, and reduces the steel's hysteresis loss. Hysteresis is the lag between the times when a magnetic field is first generated or applied to the steel and when the field fully develops. Through control of the grain size, the hysteresis loss of the steel can be accurately controlled. The direction of the grain in Silicon Steel can also affect its efficiency. The grain can be oriented in one or double direction (CRGO) through rolling to improve its density or the grain can be non-oriented and run in all directions (CRNGO), making the Silicon Steel less expensive.
Specifications
1. Grades: 50W800
2. Thickness: 0.5mm&0.65mm
3. Width: 1000mm&1200mm
4. Inner Diameter: 508mm
5. Weight of Steel Coil: 3-8MT
Parameters
1. Density: 7.8kg/dm3
2. Iron Loss: 4.507W/Kg (f=50Hz B=1.5T)
3. Magnetic Flux Strength: 1.703T (f=50Hz H=5000A/M)
4. Interlayer Resistance: >10Ω . Cm2/piece
5. Yield Strength: 250MPa
6. Tensile Strength: 360MPa
7. Extended Length 39% (380MPa)
8. HV1 Hardness: 122
8. Lamination Factor: 97%
9. Minimum number of Bends: 10Times
Width (mm) | Thickness (mm) | Thickness tolerance (mm) | Longitudinal thickness tolerance (mm) | Traverse thickness tolerance (mm) | Width Tolerance (mm) | Flatness (%) |
800-100 | 0.35 | ±0.03 | ≤0.02 | ≤0.02 | +1.5 0 | ≤2 |
0.5 | ±0.03 | ≤0.03 | ≤0.02 | |||
0.65 | ±0.04 | ≤0.03 | ≤0.03 | |||
>1000 | 0.35 | ±0.03 | ≤0.03 | ≤0.02 | +1.5 0 | |
0.5 | ±0.03 | ≤0.03 | ≤0.02 | |||
0.65 | ±0.04 | ≤0.04 | ≤0.03 |